CYANIDE COPER
| Process | Compositions& Operating Conditions | Applications & Features | |
| CN-COPPER | CS-92/CNC-97 Temperature Current Density |
80-120 g/l 50-60°C 1-2 A/dm² |
Cyanide copper bath which gives semi bright deposit, mainly used on ferrous metals as a precoating before nickel plating and for copper oxidizing finish. The bath is suitable for vat as well as barrel plating. |
| ROCHELLE COPPER | Salt RC-95 Temperature Current Density |
150 g/l 40-60°C 3-5 A/dm² |
A low pH cyanide based semi-bright copper bath mainly used as a pre-coating on zinc and aluminium based articles also used in barrel plating and vat plating. |
| HIGH SPEED COPPER | Salt CU-10 Temperature Current Density Cyano copper additive Cyano copper brightener |
150 -200 g/l 40-60°C 3-5 A/dm² 10 ml/ltr. 5-10 ml/ltr. |
Potassium Cn based copper salt for high speed lcd coverage with brightness. Specially used on Zinc and aluminium based articles for barrel as well as rack plating. |
BRIGHT ACID COPPER
| Process | Compositions& Operating Conditions | Applications & Features | |
| CUPRABRITE COPPER 3811-12 |
Copper Sulphate Sulphuric Acid Chloride Temperature Current Density ADDITIVE AC-3811 BRIGHTENER AC-3812 WETTING AGENT-3813 |
175-225 g/l 35-40 m/l 100-150 ppm 25-32°C 2-6 A/dm² 4-6 m/l 0.4-0.6 m/l 0.1-0.2 m/l |
A low cost highly bright plating with good levelling used for zinc based die casting steel & brass etc Solution maintenance is very easy mostly used for nickel free jewellery plating & plating on plastics can be used as nickel under coat for better levelling effects. |
| CUPRALITE PREMIA | Copper Sulphate Sulphuric Acid PREMIA-MAKE UP PREMIA PART-A PREMIA PART-B Chloride Temperature Current Density Wetting Agent Premia |
175-225 g/l 35-40 m/l 4-6 ml/l 0.4-0.6 m/l 0.3-0.4 m/l 100-150 ppm 25-32°C 2-6 A/dm² 0.1-0.3 m/l |
High Levelling Acid Copper Brightner System for ABS Sanitary & other Hardware items. Easier option with three part brightener system, to balance levelling and lcd coverage. |
ACID COPPER SINGLE SYSTEM
| Process | Compositions& Operating Conditions | Applications & Features | |
| CUPRAMAX Cu - 2040 DYE FREE |
Copper Sulphate Sulphuric Acid Brightener Cu-2040 Chloride Temperature Current Density Cu-2040 Leveller Wetting Agent |
175-225 g/l 35-45 ml/l 3-4 ml/l 50-100 ppm 25-35°C 2-6 A/dm² 0.2-0.3 ml/l 0.1-0.3 ml/l |
New generation dye free single brightener system with very high levelling and lcd coverage does not need regular carbon treatments.Does not create any pitting.Leveller can be used optionally to increase fast levelling. |
| DYELESS COPPER ULTRA 4040 |
Copper Sulphate Sulphuric Acid Brightener Cu-4040 Chloride Temperature Current Density Cu-4040 Leveller Wetting Agent |
175-225 g/l 35-45 ml/l 3-4 ml/l 50-100 ppm 25-35°C 2-6 A/dm² 0.2-0.3 ml/l 0.1-0.3 ml/l |
New generation dye free single brightener system with very high levelling and lcd coverage does not need regular carbon treatments.Does not create any pitting.Leveller can be used optionally to increase fast levelling. |
PYRO COPPER SYSTEM
| Process | Compositions& Operating Conditions | Applications & Features | |
| PYRO COPPER 600 | PYRO COPPER Conc. 3X PYRO COPPER CORRECTOR PYRO COPPER ADDITIVE PYRO COPPER BRIGHTENER Temperature Current Density pH AMMONIA solution(25%) anodes |
330 -350 ml/l 50-70 ml/l 8-10 ml/l 5- 8 ml/l 45-50°C 2-4 A/dm² 7.8- 8.3 4-5 ml/l OFHC COPPER |
Non cyanide alkaline based new generation copper plating with very good brightness and low density coverage in short duration. Specially used for zinc die cast and aluminium. Operating cost is very low as the efficiency of the bath is nearly 100 %. |