Acid stripper to strip nickel from copper and copper alloys does not harm the base material . After
stripping oxide filmis formed which is removed in 10% cyanide solution.
NICKEL ELECTRO STRIPPER
LD-102
Concentration
Temperature.
Current Density
Anodic Cathode
250- 300 ml/1
50-60°
10 Amp/ dm²
Lead/s.s/carbon
An Alkaline stripping bath used to strip nickel, silver, cadmium from ss specially used for removind nickel from jiggs without etching the base metal.
AURO STRIP
Concentration
Temperature
Ready to use
50-60°
Does not harm the base material and current seizes automatically when copper is achieved. A cyanide based stripper to strip gold & silver from
nickel.
NICKEL STRIPPER FOR
-M.S
Concentration
Temperature.
Time
150-200 g/l
60-70°C
2-5 mins.
Cyanide based nickel stripper salt for steel based articles. Removes nickel& Copper without etching the base.
NICKEL STRIPPER FROM
-ZINC BASE
Concentration
Temperature.
Time
Ready to use
Room
2-5 mins.
Acidic stripping chemical to remove nickel & copper from zinc based articles without etching the base
The articles should be immediately removed from the solution after stripping.
LACQUER STRIPPER
Concentration
Temperature.
Time
Ready to use
Room
2-5 mins.
Organic lacquer stripper to remove any type of lacquer coating without damaging the base plating.