Bright Silver salt
Silver brightener Ag-500 A
Silver brightener Ag-500 B
Current Density
250 g/l
50 ml/l
30 ml/l
1-2 A/dm²
It gives mirror bright and hard silver plating with anti tarnish effect. Mainly used for electrical (Switch Gear) and electronic components. Used in artificial/real Jewellery.
SILVER brightener
PROCESS -300
Bright Silver salt
Silver brightener Ag-300 A
Silver brightener Ag-300 B
Silver brightener Ag-300 C
Current Density
250 g/l
50 ml/l
30 ml/l
2-3 ml/l
1-2 A/dm²
It gives mirror bright and hard silver plating with anti tarnish effect. Additive 300-C can be used for extra whiteness. Used in artificial/real Jewellery.
STRIKE SILVER SALT-
-SSS-22
Concentration
Temperature
Time
Current Density
80 g/l
20-30°C
10-30 sec.
3-4 A/dm²
Strike silver given before main Silver to avoid immersion silver coating.
CLEANING PROCESS -
-AFTER SILVER
After Silver Cleaning 'A'
After Silver Cleaning 'B'
5-10 g/l
5-10 g/l
Cleaning process after silver plating to remove cyanide spillage.
VIBRO CLEAN
CONCENTRATION
0.5 gm/ltr.
To be added in vibrator polishing for jewellery. Mostly used for silver plated articles, keeps SS balls and pins cleaned during vibrator polishing
SILVER EX AG
ANTI TARNISH FOR
SILVER
Silverex Ag
Temperature
Time
100-200 ml/l
30-40°C
1-2 mins.
A solvent free emulsion Anti tarnish for silver deposit does not contain Halogeneted Hydrocarbon solvent. used as a Dip Process.
SILCHROMATE
Concentration
Temperature
Time
Voltage
Cathodic Anodes
80-100 ml/l
40-50°C
1-2 mins.
4-5 V
S.S. or Carbon
A chrome based electrolytic passivation for silver plated articles. Gives a very long life and cost effective. Anti tarnish
coating most suitable for electronic/ electrical industry.