ALKALINE SOAK CLEANERS
| Process | Compositions& Operating Conditions | Applications & Features | |
| ULTRA SOAK CLEANER-56 | Ultra Soak Cleaner US-56 Temperature Time |
80-100 gm/l 70-80°C 2-3 mins |
High Power Alkaline Soak Cleaner for Zinc die cast, Silver, Aluminium Non-ferrous metals specially used in Ultrasonic Cleaning Machines. |
| ULTRASOAKCLEAN US-156 | Ultra Soak Cleaner US-156 Temperature Time |
80-100 gm/l 70-80°C 2-3 mins |
High Power Alkaline Soak Cleaner for Mild Steel, Stainless Steel used in Ultrasonic Cleaning Machines. |
| STEELO P-20 | STEELO P-20 Temperature Time |
80-100 gm/l 70-80°C 2-3 mins |
High Power Alkaline Soak Cleaner for Mild Steel, Stainless Steel, Zinc and Zinc Alloys used in Ultrasonic Cleaning Machines. |
ALKALINE ELECTROLYTIC CLEANERS
| Process | Compositions& Operating Conditions | Applications & Features | |
| BRASSOCLEAN ELECTROLYTIC CLEANER FOR BRASS |
Brassoclean BC-54 Temperature Time Current Density |
100-120 g/l 50-60°C 1-2 mins. 5-10 A/dm² |
Heavy duty cathodic alkaline cleaner for Copper Alloys. Can be used as anodic cleaner also does not harm the polished surface. |
| ZINCO CLEAN ELECTROLYTIC CLEANER FOR ZINC/ALUMINIUM |
Zinco Clean Temperature Time Current Density |
80-100 g/l 40-50°C 1-2 mins. 2.5-5 A/dm² |
Light electro cleaner (cathodic) for zinc base die casting and aluminium does not harm the zinc surface. |
| FERROCLEAN FOR FERROUS METALS ANODIC |
Ferro Clean Fe-600 Temperature Time Current Density |
100-125 g/l 40-50°C 2-3 mins. 3-5 A/dm² |
Heavy duty cleaner for ferrous metals removes oil, grease & rust. |
DIP POLISH
| Process | Compositions& Operating Conditions | Applications & Features | |
| ACID CLEANER FOR COPPER & COPPER ALLOYS |
Concentration Temperature Time |
80-100 ml/l Room 1-2 mins. |
Removes oxide film from cu & cu alloys, as well as cleans the surface. |
| BRIGHT POLISH FOR BRASS BY DIP PROCESS |
Brass Dip Polish BP-99 Temperature Time |
Ready to use Room 30-60 sec. |
Bright polish for intricated shaped copper and copper alloys. does not attack the base metal polishes the surface & produces a glossy finish. |
| BRASS MATT POLISH | Brass Cutting Polish Hydrogen Peroxide (35%) Temperature Time |
50-100 ml/ltr. 150-300 ml/ltr. 30-40°C 1-5 mins. |
Fine cutting action on brass to give a uniform matt finish like sand blasting . A dip in 5% sulphuric acid is used after brass matt polish to remove the oxide film |
| BRASS POLISH BP-66 | BP-66 Hydrogen Peroxide Temperature Time |
50-100 ml/ltr. 100-300 ml/ltr. Room 3-4 min. |
Very bright polish can be achieved on small brass parts. Specially suitable for parts to be barrel plated. A brown oxide film will be formed on parts which can be removed by rinsing in 5% Sulphuric Acid. |
| BRIGHT ZINC POLISH ZP- 150 |
ZP-150 Temperature Time |
Ready to use Room 2-5 min. |
Bright polish for intricate shaped zinc articles. Does not attack the base metal polishes the surface & produces a glossy finish. |
| MICRO ETCHING PICTAX | Conc. Temperature Time |
50-100 gms/ltr. Room 30 sec.-1 min. |
Powder form acid activation for Zinc die cast
components,can be used as a replacement for sulphuric acid and hydrofluoric acid. Creates very fine etching on surface for better adhesion. |
| AQUA PREP 1002 | Conc. Temperature Time |
100-200 ml/ltr. 30-40°C 1-2 min. |
Water based anti rust coating for steel. |