Solvent based, transparent lacquer system to provide tough, durable organic coatings. Can be used on silver, brass, tin, copper and nickel free plated articles. With SST of more than 400 hrs.
ACRYSIL
Concentration
Temperature
Time
100-300 ml/l
Room
20-30 sec.
Water dilutable lacquer coating, High corrosion resistance gives clear transparent coating. Increases SST life for more than 100 -150 hrs.
PROTECT -20 BLACK
TOP COAT
Concentration
Temperature
Time
Ready to use
Room
20-30 sec.
Solvent based, black lacquer system to provide a bright dark black organic coatings to enhance the color and SST life for more than 200 hrs
AQUA POLY GUARD
HG-5000
CLEAR-TOP COAT
Concentration
PH
Time
200-400 ml/l
8.5-9.5
20-60 sec.
A high gloss clear organic top coat to form a transparent film on plated articles to increase the SST life for components.
AQUA GUARD
HG-3000
CLEAR-TOP COAT
Concentration
PH
Time
200-400 ml/l
8.5-9.5
20-30 sec.
A high gloss top coat to form a transparent inorganic/organic film on plated parts.
BLACK SEALER
Concentration
Temperature
Time
100-300 ml/l
Room
20-30 sec.
A range of post passivation black sealer process to achieve appealing attractive finish, on passivated zinc plated components.
POST DIP BLACK
STABILIZER
Concentration
Time
Temperature
100 ml- 200 ml
10sec-20 sec
40-45°C
Stabilizes the colour of black passivation and improves the SST life and gloss.
POLYGRAND HG-9000
Concentration
PH
Time
200-400 ml/l
8.5-9.5
20-30 sec.
A high gloss topcoat to give a glossy organic film with very good adhesion & salt spary life.
NANO CLEAR
Concentration
Temperature
Time
100-200 ml/l
Room
10-20 sec.
Water based Topcoat with very good scratch resistance and self healing properties. Gives a very good hard coating on the surface.
SP - 300
Concentration
Temperature
Time
200-300 ml/l
Room
10-20 sec.
Water based inorganic topcoat with very good hardness.